Nikèl alliages manyèl lektwòd ENiCu-7 soudure done
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Ni | Fe | Ti | Cu | P | S |
| RÈG GB/T | 0.15 | 4.00 | 1.50 | ≥62 | 2.50 | 1.00 | 27-34 | 0.02 | 0.015 |
| RÈG AWS | 0.15 | 4.00 | 1.50 | 62-69 | 2.50 | 1.00 | Marge | 0.02 | 0.015 |
| EGZANP VALÈ | 0.021 | 3.3 | 0.83 | 67.4 | 0.5 | 0.42 | 27.3 | 0.009 | 0.007 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
| RÈG GB/T | 200 | 480 | - | 27 | ||||
| RÈG AWS | - | 480 | - | 30 | ||||
| EGZANP VALÈ | 360 | 485 | - | 39.5 | ||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 2.6 * 300 | 3.2 * 350 | 4.0 * 350 | |||||||
| ELEKTRISITE (Amp) | H/W | 65-95 | 70-115 | 95-145 | ||||||
Low idwojèn kalite men elektwòd, nominal konpozisyon (pousan pwa) se 66Ni-30Cu-3Mn-1Fe, pou elektwòd alyaj nikèl-kwiv.
Akòz kantite lajan ki apwopriye nan Mn ak Ti ka efektivman anpeche jenerasyon an nan fant tèmik ak porositë.
Ki estab arc, bèl fòme, ti Splash, fasil retire salop, bon rezistans porosite, pwopriyete yo mekanik nan metal fonn se ki estab.
-
Inner Mongoli Xinao enèji co, LTD.3 * 3000m³ ba tanperati tank esferik
-
Materyèl soude pou resipyan
-
3000m fon lanmè semi-submersible platfòm perçage "Haiyang Shiyou 981"
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Ni | Fe | Ti | Cu | P | S |
| RÈG GB/T | 0.15 | 4.00 | 1.50 | ≥62 | 2.50 | 1.00 | 27-34 | 0.02 | 0.015 |
| RÈG AWS | 0.15 | 4.00 | 1.50 | 62-69 | 2.50 | 1.00 | Marge | 0.02 | 0.015 |
| EGZANP VALÈ | 0.021 | 3.3 | 0.83 | 67.4 | 0.5 | 0.42 | 27.3 | 0.009 | 0.007 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
| RÈG GB/T | 200 | 480 | - | 27 | ||||
| RÈG AWS | - | 480 | - | 30 | ||||
| EGZANP VALÈ | 360 | 485 | - | 39.5 | ||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 2.6 * 300 | 3.2 * 350 | 4.0 * 350 | |||||||
| ELEKTRISITE (Amp) | H/W | 65-95 | 70-115 | 95-145 | ||||||