Nikèl alliages manyèl lektwòd ENi-1 soude fabrication makings
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Ni | Fe | Ti | Cu | P | S |
| RÈG GB/T | 0.10 | 0.75 | 1.20 | ≥92 | 0.70 | 1.0-4.0 | 0.20 | 0.02 | 0.015 |
| RÈG AWS | 0.10 | 0.75 | 1.25 | ≥92 | 0.75 | 1.0-4.0 | 0.25 | 0.03 | 0.02 |
| EGZANP VALÈ | 0.046 | 0.06 | 0.82 | 95.5 | 0.12 | 2.7 | 0.01 | 0.007 | 0.001 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
| RÈG GB/T | 200 | 410 | - | 18 | ||||
| RÈG AWS | - | 410 | - | 20 | ||||
| EGZANP VALÈ | 310 | 435 | - | 29 | ||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 2.6 * 300 | 3.2 * 350 | 4.0 * 350 | |||||||
| ELEKTRISITE (Amp) | H/W | 65-95 | 70-115 | 95-145 | ||||||
Titàn-kalsyòm lektwòd men, nominal konpozisyon (pousan pa pwa) se 95Ni-2.5Ti.
Ki estab arc, bèl fòme, ti Splash, fasil retire salop, bon rezistans porosite.
Metal la fusion gen bon pwopriyete mekanik, rezistans chalè, rezistans korozyon, fizyon ak rezistans krak.
Cr-Mo asye seri materyèl soude ak elektwòd sifas materyèl soude yo lajman ki itilize nan ekipman raffinage petwòl.
-
158,000 tòn tanker Suez
Supercore SG
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Ni | Fe | Ti | Cu | P | S |
| RÈG GB/T | 0.10 | 0.75 | 1.20 | ≥92 | 0.70 | 1.0-4.0 | 0.20 | 0.02 | 0.015 |
| RÈG AWS | 0.10 | 0.75 | 1.25 | ≥92 | 0.75 | 1.0-4.0 | 0.25 | 0.03 | 0.02 |
| EGZANP VALÈ | 0.046 | 0.06 | 0.82 | 95.5 | 0.12 | 2.7 | 0.01 | 0.007 | 0.001 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
| RÈG GB/T | 200 | 410 | - | 18 | ||||
| RÈG AWS | - | 410 | - | 20 | ||||
| EGZANP VALÈ | 310 | 435 | - | 29 | ||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 2.6 * 300 | 3.2 * 350 | 4.0 * 350 | |||||||
| ELEKTRISITE (Amp) | H/W | 65-95 | 70-115 | 95-145 | ||||||