Nikèl alyaj TIG ERNiCrMo-3 Soudure materyèl
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
| RÈG GB/T | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.0-4.2 | - | - |
| RÈG AWS | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.15-4.15 | 0.02 | 0.015 |
| EGZANP VALÈ | 0.006 | 0.15 | 0.12 | 22.02 | 64.84 | 8.75 | 0.18 | 3.49 | 0.001 | 0.001 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
| RÈG GB/T | - | - | - | - | ||||
| RÈG AWS | - | - | - | - | ||||
| EGZANP VALÈ | - | 790 | 159/-196 | 46 | ||||
Nikèl-chromium-molybdène nikèl-baz alyaj gaz soude fil, nominal konpozisyon se 61%Ni-22%Cr-9%Mo-3.5%Nb + Ta.
Metal fonn gen bon pwopriyete mekanik ak bon rezistans nan korozyon pitting ak korozyon fant.
Ki estab arc, bèl fòme, bon koule nan fè fonn, ak ekselan pèfòmans pwosesis soude.
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
| RÈG GB/T | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.0-4.2 | - | - |
| RÈG AWS | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.15-4.15 | 0.02 | 0.015 |
| EGZANP VALÈ | 0.006 | 0.15 | 0.12 | 22.02 | 64.84 | 8.75 | 0.18 | 3.49 | 0.001 | 0.001 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
| RÈG GB/T | - | - | - | - | ||||
| RÈG AWS | - | - | - | - | ||||
| EGZANP VALÈ | - | 790 | 159/-196 | 46 | ||||