Nikèl alliages MIG ERNiCrMo-3 soudure makings
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
| RÈG GB/T | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.0-4.2 | - | - |
| RÈG AWS | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.15-4.15 | 0.02 | 0.02 |
| EGZANP VALÈ | 0.006 | 0.15 | 0.15 | 22.01 | 64,80 | 8.72 | 0.18 | 3.49 | 0.001 | 0.001 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
| RÈG GB/T | - | - | - | - | ||||
| RÈG AWS | - | - | - | - | ||||
| EGZANP VALÈ | - | 780 | 144/-196 | 45 | ||||
Nikèl-chromium-molybdène nikèl-baz alyaj gaz soude fil, nominal konpozisyon se 61%Ni-22%Cr-9%Mo-3.5%Nb + Ta.
Bon pwopriyete mekanik ak rezistans nan pitting ak korozyon fant nan metal fonn.
Lis fil manje, arc ki estab, bèl fòme, bon koule nan metal cho, mwens Splash, ak ekselan pèfòmans pwosesis soude.
-
Lachin Global Demethane Tower
-
Zhejiang Petrochemical dyezèl / lwil brit tank depo
-
300,000-tòn lanmè Pwodiksyon k ap flote ak tankè depo (FPSO)
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
| RÈG GB/T | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.0-4.2 | - | - |
| RÈG AWS | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.15-4.15 | 0.02 | 0.02 |
| EGZANP VALÈ | 0.006 | 0.15 | 0.15 | 22.01 | 64,80 | 8.72 | 0.18 | 3.49 | 0.001 | 0.001 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
| RÈG GB/T | - | - | - | - | ||||
| RÈG AWS | - | - | - | - | ||||
| EGZANP VALÈ | - | 780 | 144/-196 | 45 | ||||