KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Cr | Ni | Fe | Nb+Ta | P | S | |
RÈG GB/T | 0.10 | 5.0-10.0 | 1.00 | 13.0-17.0 | ≥60 | 10.00 | 1.0-3.5 | 0.02 | 0.015 | |
RÈG AWS | 0.10 | 5.0-9.5 | 1.00 | 13.0-17.0 | ≥59 | 10.00 | 1.0-2.5 | 0.03 | 0.015 | |
EGZANP VALÈ | 0.046 | 7.6 | 0.45 | 15.7 | 15.7 | 3.56 | 1.76 | 0.005 | 0.004 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
RÈG GB/T | 360 | 550 | - | 27 | ||||
RÈG AWS | - | 550 | - | 30 | ||||
EGZANP VALÈ | 410 | 650 | - | 40 |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 2.6 * 300 | 3.2 * 350 | 4.0 * 350 | ||||||||
ELEKTRISITE (Amp) | H/W | 69-95 | 70-115 | 95-145 | |||||||
O/W | 55-80 | 65-110 | 80-130 |
Low idwojèn tip men elektwòd, nominal konpozisyon (pousan pwa) se 65Ni-15Cr-8Fe-7.5Mn-2Nb + Ta, pou elektwòd alyaj nikèl-chrome-fè.
Akòz kontni an segondè nan alyaj la, li gen gwo fòs tanperati ki wo ak rezistans oksidasyon epi li ka adapte yo ak seri tanperati ki soti nan tanperati ki ba a 480 ℃.
Ki estab arc, bèl fòme, ti Splash, fasil retire salop, bon rezistans porosite, pwopriyete yo mekanik nan metal fonn se ki estab.
-
300,000-tòn lanmè Pwodiksyon k ap flote ak Tank Depo (FPSO)
Harbin elektrik twa pòt CMT
-
Zhejiang Satellite Energy 3 × 60,000 m³LPG tank depo
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Cr | Ni | Fe | Nb+Ta | P | S | |
RÈG GB/T | 0.10 | 5.0-10.0 | 1.00 | 13.0-17.0 | ≥60 | 10.00 | 1.0-3.5 | 0.02 | 0.015 | |
RÈG AWS | 0.10 | 5.0-9.5 | 1.00 | 13.0-17.0 | ≥59 | 10.00 | 1.0-2.5 | 0.03 | 0.015 | |
EGZANP VALÈ | 0.046 | 7.6 | 0.45 | 15.7 | 15.7 | 3.56 | 1.76 | 0.005 | 0.004 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
RÈG GB/T | 360 | 550 | - | 27 | ||||
RÈG AWS | - | 550 | - | 30 | ||||
EGZANP VALÈ | 410 | 650 | - | 40 |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 2.6 * 300 | 3.2 * 350 | 4.0 * 350 | ||||||||
ELEKTRISITE (Amp) | H/W | 69-95 | 70-115 | 95-145 | |||||||
O/W | 55-80 | 65-110 | 80-130 |