Alyaj nikèl Flux fil nwayo ENiCrMo3T1-4 koneksyon soude
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Cr | Ni | Fe | Nb | Mo | P | S |
| RÈG GB/T | - | - | - | - | - | - | - | - | - | - |
| RÈG AWS | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58.0 | 5.00 | 3.15-4.15 | 8.0-10.0 | 0.02 | 0.02 |
| EGZANP VALÈ | 0.015 | 0.25 | 0.3 | 22 | 64.00 | 0.3 | 3.3 | 9.5 | 0.0005 | 0.0005 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
| RÈG GB/T | - | - | - | - | ||||
| RÈG AWS | - | 690 | - | 25 | ||||
| EGZANP VALÈ | - | 760 | 80/-196 | 32 | ||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 1.2 | ||||
| Volt | 25-34 | ||||
| Amp | 150-250 | ||||
| Longè ekstansyon sèk (mm) | 15-25 | ||||
| Koule gaz (l/min) | 20-25 | ||||
Konpozisyon nominal la te 60%Ni-22%Cr-9%Mo-3%Fe-3.6%Nb.
-196 ° C pèfòmans enpak tanperati ki ba se ekselan.
Arc la se mou ak ki estab, mwens Splash, bèl fòme, bon retire salop, ki estab fil manje, ak ekselan pèfòmans pwosesis soude.
-
Aplikasyon pou pouvwa tèmik
-
Qinghai Youjian Wunan Oilfield
-
20000TEU veso bato
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Cr | Ni | Fe | Nb | Mo | P | S |
| RÈG GB/T | - | - | - | - | - | - | - | - | - | - |
| RÈG AWS | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58.0 | 5.00 | 3.15-4.15 | 8.0-10.0 | 0.02 | 0.02 |
| EGZANP VALÈ | 0.015 | 0.25 | 0.3 | 22 | 64.00 | 0.3 | 3.3 | 9.5 | 0.0005 | 0.0005 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
| RÈG GB/T | - | - | - | - | ||||
| RÈG AWS | - | 690 | - | 25 | ||||
| EGZANP VALÈ | - | 760 | 80/-196 | 32 | ||||
REKÒMANDE PARAMÈ SOUDES:
| DYAMET SPECIFICATIONS (mm) | 1.2 | ||||
| Volt | 25-34 | ||||
| Amp | 150-250 | ||||
| Longè ekstansyon sèk (mm) | 15-25 | ||||
| Koule gaz (l/min) | 20-25 | ||||