Nikèl alyaj TIG ERNi-1 Koneksyon soude
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | Fe | Ti | P | S |
| RÈG GB/T | 0.15 | 1.00 | 0.70 | - | ≥92 | - | 1.0 | 2.0-3.5 | 0.03 | 0.015 |
| RÈG AWS | 0.15 | 1.00 | 0.75 | - | ≥93 | - | 1.0 | 2.0-3.5 | 0.03 | 0.015 |
| EGZANP VALÈ | 0.005 | 0.48 | 0.26 | 0.46 | 94.69 | 0.001 | 0.07 | 2.95 | 0.001 | 0.001 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
| RÈG GB/T | - | - | - | - | ||||
| RÈG AWS | - | - | - | - | ||||
| EGZANP VALÈ | - | 550 | 276/-196 | 36 | ||||
Pi nikèl fil soude gaz, konpozisyon nominal se 96% Ni-3% Ti.
Akòz adisyon a ase eleman Ti, porosite a ka efektivman redwi nan pwosesis la soude.
Ki estab arc, bèl fòme, bon koule nan fè fonn, ak ekselan pèfòmans pwosesis soude.
-
37,000 tòn bato kago jeneral
-
JU2000E jack-up perçage mare
-
Bwat piki sekirite
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | Fe | Ti | P | S |
| RÈG GB/T | 0.15 | 1.00 | 0.70 | - | ≥92 | - | 1.0 | 2.0-3.5 | 0.03 | 0.015 |
| RÈG AWS | 0.15 | 1.00 | 0.75 | - | ≥93 | - | 1.0 | 2.0-3.5 | 0.03 | 0.015 |
| EGZANP VALÈ | 0.005 | 0.48 | 0.26 | 0.46 | 94.69 | 0.001 | 0.07 | 2.95 | 0.001 | 0.001 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
| RÈG GB/T | - | - | - | - | ||||
| RÈG AWS | - | - | - | - | ||||
| EGZANP VALÈ | - | 550 | 276/-196 | 36 | ||||