KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
RÈG GB/T | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67.0 | - | 3.0 | 2.0-3.0 | - | - |
RÈG AWS | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67.0 | - | 3.0 | 2.0-3.0 | 0.03 | 0.015 |
EGZANP VALÈ | 0.024 | 2.78 | 0.05 | 20.69 | 72.85 | 0.15 | 0.67 | 2.44 | 0.001 | 0.001 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
RÈG GB/T | - | - | - | - | ||||
RÈG AWS | - | - | - | - | ||||
EGZANP VALÈ | - | 710 | 170-196 | 39 |
Nikèl-chromium-fè nikèl-baz alyaj gaz soude fil, nominal konpozisyon se 72%Ni-20%Cr-3%Mn-2.5%Nb + Ta.
Metal la fusion gen bon pwopriyete mekanik, bon rezistans korozyon, segondè rezistans oksidasyon ak fòs ranpe.
Ki estab arc, bèl fòme, bon koule nan fè fonn, ak ekselan pèfòmans pwosesis soude.
-
Qinghai Youjian Wunan Oilfield
-
Materyèl soude pou boutèy machin LNG
-
Chofaj presyon ki wo nan Hangzhou Boiler Group Co LTD
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
RÈG GB/T | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67.0 | - | 3.0 | 2.0-3.0 | - | - |
RÈG AWS | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67.0 | - | 3.0 | 2.0-3.0 | 0.03 | 0.015 |
EGZANP VALÈ | 0.024 | 2.78 | 0.05 | 20.69 | 72.85 | 0.15 | 0.67 | 2.44 | 0.001 | 0.001 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
RÈG GB/T | - | - | - | - | ||||
RÈG AWS | - | - | - | - | ||||
EGZANP VALÈ | - | 710 | 170-196 | 39 |