Nikèl alliages manyèl lektwòd ENiCrFe-9 Welding makings
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Fe | Cr | Ni | Mo | Cu | Nb+Ta | |
| RÈG GB/T | 0.15 | 1.0-4.5 | 0.80 | 12.00 | 12.0-17.0 | ≥55 | 2.5-5.5 | 0.50 | 0.5-3.0 | |
| RÈG AWS | 0.15 | 1.0-4.5 | 0.75 | 12.00 | 12.0-17.0 | ≥55 | 2.5-5.5 | 0.50 | 0.5-3.0 | |
| EGZANP VALÈ | 0.07 | 2.6 | 0.28 | 4.03 | 14.3 | 66.6 | 4.41 | 0.060 | 1.67 | |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
| RÈG GB/T | 360 | 650 | - | 18 | ||||
| RÈG AWS | - | 650 | - | 25 | ||||
| EGZANP VALÈ | 460 | 680 | - | 41.5 | ||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 2.6 * 300 | 3.2 * 350 | 4.0 * 350 | ||||||||
| ELEKTRISITE (Amp) | H/W | 69-95 | 70-115 | 95-145 | |||||||
| O/W | 55-80 | 65-110 | 80-130 | ||||||||
Low idwojèn tip men elektwòd, nominal konpozisyon (pousan pa pwa) se Ni14Cr4FeNbMo, nikèl - chromium - elektwòd alyaj fè.
Arc ki estab, bèl fòme, ti kras Splash, fasil retire salop.
Bon rezistans porosite, pwopriyete yo mekanik nan metal fonn se ki estab.
-
Nanjing Chengzhi Yongqing Enèji 07MnNiMoDR asye ethylene boul tank
Entèn raktor
-
Aktik LNG-2 pwojè
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Fe | Cr | Ni | Mo | Cu | Nb+Ta | |
| RÈG GB/T | 0.15 | 1.0-4.5 | 0.80 | 12.00 | 12.0-17.0 | ≥55 | 2.5-5.5 | 0.50 | 0.5-3.0 | |
| RÈG AWS | 0.15 | 1.0-4.5 | 0.75 | 12.00 | 12.0-17.0 | ≥55 | 2.5-5.5 | 0.50 | 0.5-3.0 | |
| EGZANP VALÈ | 0.07 | 2.6 | 0.28 | 4.03 | 14.3 | 66.6 | 4.41 | 0.060 | 1.67 | |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
| RÈG GB/T | 360 | 650 | - | 18 | ||||
| RÈG AWS | - | 650 | - | 25 | ||||
| EGZANP VALÈ | 460 | 680 | - | 41.5 | ||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 2.6 * 300 | 3.2 * 350 | 4.0 * 350 | ||||||||
| ELEKTRISITE (Amp) | H/W | 69-95 | 70-115 | 95-145 | |||||||
| O/W | 55-80 | 65-110 | 80-130 | ||||||||