Nikèl alliages TIG ERNiCrFe-7A Joint soudure
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
RÈG GB/T | - | - | - | - | - | - | - | - | - | - |
RÈG AWS | 0.04 | 1.00 | 0.50 | 28.0-31.5 | Rem | 0.50 | 7.0-11.0 | 0.5-1.0 | 0.02 | 0.015 |
EGZANP VALÈ | 0.028 | 0.15 | 0.11 | 29.8 | 59.03 | 0.06 | 9.8 | 0.86 | 0.001 | 0.002 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | Tretman chalè | ||||||
RÈG GB/T | - | - | - | - | - | ||||||
RÈG AWS | - | - | - | - | - | ||||||
EGZANP VALÈ | - | 760 | 133/Tanperati chanm | 37 | 607 °C * 25h |
Nikèl-chromium-fè nikèl-baz alyaj gaz soude fil, nominal konpozisyon se 60%Ni-29%Cr-9%Fe-0.75%Nb.
Bon pwopriyete mekanik nan metal fonn, espesyalman rezistans nan fann plastik ki ba (DDC).
Segondè kontni Cr fè li gen ekselan rezistans estrès korozyon fann nan anviwònman dlo pi anba kondisyon radyasyon. Ki estab arc, bèl fòme, bon koule nan fè fonn, ak ekselan pèfòmans pwosesis soude.
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
RÈG GB/T | - | - | - | - | - | - | - | - | - | - |
RÈG AWS | 0.04 | 1.00 | 0.50 | 28.0-31.5 | Rem | 0.50 | 7.0-11.0 | 0.5-1.0 | 0.02 | 0.015 |
EGZANP VALÈ | 0.028 | 0.15 | 0.11 | 29.8 | 59.03 | 0.06 | 9.8 | 0.86 | 0.001 | 0.002 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | Tretman chalè | ||||||
RÈG GB/T | - | - | - | - | - | ||||||
RÈG AWS | - | - | - | - | - | ||||||
EGZANP VALÈ | - | 760 | 133/Tanperati chanm | 37 | 607 °C * 25h |