Alyaj nikèl manyèl elektwòd ENiCrMo-13 done fabwikasyon soude
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | Fe | P | S |
| RÈG GB/T | 0.02 | 1.00 | 0.20 | 22.0-24.0 | ≥56 | 15.0-16.5 | 1.50 | 0.02 | 0.015 |
| RÈG AWS | 0.02 | 1.00 | 0.20 | 22.0-24.0 | Marge | 15.0-16.5 | 1.50 | 0.02 | 0.01 |
| EGZANP VALÈ | 0.018 | 0.5 | 0.15 | 22.5 | 60.31 | 15.5 | 1 | 0.005 | 0.004 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
| RÈG GB/T | 350 | 690 | - | 22 | ||||
| RÈG AWS | - | 690 | - | 25 | ||||
| EGZANP VALÈ | 520 | 750 | - | 32 | ||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 2.6 * 300 | 3.2 * 350 | 4.0 * 350 | |||||||
| ELEKTRISITE (Amp) | H/W | 65-95 | 70-115 | 95-145 | ||||||
| O/W | 55-80 | 60-110 | 90-35 | |||||||
Low idwojèn tip men elektwòd, nominal konpozisyon (pousan pwa) se 59Ni-23Cr-16Mo-1Fe, nikèl-chromium-molybdenum alyaj elektwòd.
Arc ki estab, bèl fòme, ti kras Splash, fasil retire salop.
Bon rezistans porosite, pwopriyete yo mekanik nan metal fonn se ki estab.
-
308,000 tòn VLCC lwil brit bato
-
JU2000E platfòm perçage jack-up
-
Zhejiang Satellite Energy 3 × 60,000 m³LPG tank depo
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | Fe | P | S |
| RÈG GB/T | 0.02 | 1.00 | 0.20 | 22.0-24.0 | ≥56 | 15.0-16.5 | 1.50 | 0.02 | 0.015 |
| RÈG AWS | 0.02 | 1.00 | 0.20 | 22.0-24.0 | Marge | 15.0-16.5 | 1.50 | 0.02 | 0.01 |
| EGZANP VALÈ | 0.018 | 0.5 | 0.15 | 22.5 | 60.31 | 15.5 | 1 | 0.005 | 0.004 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
| RÈG GB/T | 350 | 690 | - | 22 | ||||
| RÈG AWS | - | 690 | - | 25 | ||||
| EGZANP VALÈ | 520 | 750 | - | 32 | ||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 2.6 * 300 | 3.2 * 350 | 4.0 * 350 | |||||||
| ELEKTRISITE (Amp) | H/W | 65-95 | 70-115 | 95-145 | ||||||
| O/W | 55-80 | 60-110 | 90-35 | |||||||