Nikèl alyaj manyèl electrode ENiCrFe-4 done soude
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Cr | Ni | Fe | Nb+Ta | P | S | Mo | ||
RÈG GB/T | 0.20 | 1.0-5.0 | 1.00 | 13.0-17.0 | ≥60 | 12.00 | 1.0-3.5 | 0.02 | 0.015 | 1-3.5 | ||
RÈG AWS | 0.20 | 1.0-3.5 | 1.00 | 13.0-17.0 | ≥60 | 12.00 | 1.0-3.5 | 0.03 | 0.02 | 1-3.5 | ||
EGZANP VALÈ | 0.09 | 2.8 | 0.37 | 15.35 | 70.75 | 6.05 | 1.82 | 0.070 | 0.005 | 2.43 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
RÈG GB/T | 360 | 650 | - | 18 | ||||
RÈG AWS | - | 650 | - | 20 | ||||
EGZANP VALÈ | 464 | 727 | - | 38 |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 2.6 * 300 | 3.2 * 350 | 4.0 * 350 | ||||||||
ELEKTRISITE (Amp) | H/W | 69-95 | 70-115 | 95-145 | |||||||
O/W | 55-80 | 65-110 | 80-130 |
Low H idwojèn kalite men elektwòd, nominal konpozisyon (pwa fraksyon blan) se 7UNI-15ur-ore-2.OMIl -2. uiWu + Ta-2.5Mo, nikèl - chromium - elektwòd alyaj fè.
Ki estab arc, bèl fòme, ti Splash, fasil retire salop, bon rezistans porosite.
Pwopriyete yo mekanik nan metal la fonn se ki estab, fòs li yo pi wo pase kategori ENiCrFe-2.
-
GDS-2209/GXS-E330 tib sifas sit
-
Materyèl soude pou boutèy machin LNG
-
Shanghai Morimatsu Depo tank
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Cr | Ni | Fe | Nb+Ta | P | S | Mo | ||
RÈG GB/T | 0.20 | 1.0-5.0 | 1.00 | 13.0-17.0 | ≥60 | 12.00 | 1.0-3.5 | 0.02 | 0.015 | 1-3.5 | ||
RÈG AWS | 0.20 | 1.0-3.5 | 1.00 | 13.0-17.0 | ≥60 | 12.00 | 1.0-3.5 | 0.03 | 0.02 | 1-3.5 | ||
EGZANP VALÈ | 0.09 | 2.8 | 0.37 | 15.35 | 70.75 | 6.05 | 1.82 | 0.070 | 0.005 | 2.43 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
RÈG GB/T | 360 | 650 | - | 18 | ||||
RÈG AWS | - | 650 | - | 20 | ||||
EGZANP VALÈ | 464 | 727 | - | 38 |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 2.6 * 300 | 3.2 * 350 | 4.0 * 350 | ||||||||
ELEKTRISITE (Amp) | H/W | 69-95 | 70-115 | 95-145 | |||||||
O/W | 55-80 | 65-110 | 80-130 |