KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Ni | Cr | Mo | V | P | S |
RÈG GB/T | 0.12 | 0.40-1.25 | 0.80 | 0.8-1.10 | 0.15 | 0.35 | 0.05 | 0.03 | 0.03 |
RÈG AWS | 0.12 | 0.40-1.25 | 0.80 | 0.8-1.10 | 0.15 | 0.35 | 0.05 | 0.03 | 0.03 |
EGZANP VALÈ | 0.07 | 1.02 | 0.4 | 1.02 | 0.05 | 0.05 | 0.003 | 0.012 | 0.007 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | Tretman chalè °Cxh | |||||
RÈG GB/T | 470-550 | 550 | 27/-40 | 20 | AW | |||||
RÈG AWS | 470-550 | 550 | 27/-40 | 24 | AW | |||||
EGZANP VALÈ | 495 | 585 | 135/-40 | 26 | AW |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 2.6 * 350 | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | ||||
ELEKTRISITE (Amp) | H/W | 80-110 | 100-130 | 130-180 | 170-210 | |||
O/W | 60-100 | 80-120 | 120-160 | - |
Iron poud ba idwojèn potasyòm kalite men elektwòd, akòz adisyon a nan poud fè, segondè efikasite k ap fonn.
Severite enpak metal la fonn nan -40 ℃ tanperati k ap travay se ekselan.
Ki estab arc, mwens Splash, bon fòme, fasil retire salop, pèfòmans X-Ray se ekselan.
-
Aktik LNG-2 pwojè
-
Pwojè Kanada LNG
-
Shaanxi Pucheng -50 ℃ pwopan pwojè tank esferik
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Ni | Cr | Mo | V | P | S |
RÈG GB/T | 0.12 | 0.40-1.25 | 0.80 | 0.8-1.10 | 0.15 | 0.35 | 0.05 | 0.03 | 0.03 |
RÈG AWS | 0.12 | 0.40-1.25 | 0.80 | 0.8-1.10 | 0.15 | 0.35 | 0.05 | 0.03 | 0.03 |
EGZANP VALÈ | 0.07 | 1.02 | 0.4 | 1.02 | 0.05 | 0.05 | 0.003 | 0.012 | 0.007 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | Tretman chalè °Cxh | |||||
RÈG GB/T | 470-550 | 550 | 27/-40 | 20 | AW | |||||
RÈG AWS | 470-550 | 550 | 27/-40 | 24 | AW | |||||
EGZANP VALÈ | 495 | 585 | 135/-40 | 26 | AW |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 2.6 * 350 | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | ||||
ELEKTRISITE (Amp) | H/W | 80-110 | 100-130 | 130-180 | 170-210 | |||
O/W | 60-100 | 80-120 | 120-160 | - |