Ba-alyaj asye Manyèl elektwòd E7015-C2L Done soude
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | P | S |
| RÈG GB/T | 0.05 | 1.25 | 0.50 | - | 3.00-3.75 | - | 0.03 | 0.03 |
| RÈG AWS | 0.05 | 1.25 | 0.50 | - | 3.00-3.75 | - | 0.03 | 0.03 |
| EGZANP VALÈ | 0.04 | 0.65 | 0.23 | 0.035 | 3.52 | 0.01 | 0.005 | 0.003 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | Tretman chalè °Cxh | |||||
| RÈG GB/T | 390 | 490 | 27/-100 | 20 | 605*1 | |||||
| RÈG AWS | 390 | 490 | 27/-100 | 22 | 605*1 | |||||
| EGZANP VALÈ | 460 | 550 | 61/-100 | 31 | 605*1 | |||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 2.6 * 350 | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | ||||
| ELEKTRISITE (Amp) | H/W | 80-110 | 100-130 | 130-180 | 170-210 | |||
| O/W | 60-100 | 80-120 | 120-160 | - | ||||
Konpozisyon prensipal la se 3.5% Ni asye.
Po dwòg ki ba idwojèn potasyòm, CLADDING an metal nan -100 ° C gen severite enpak ekselan.
Ki estab arc, mwens Splash, bon fòme, fasil retire salop, pèfòmans X-Ray se ekselan.
-
Sichuan Youjian Lunnan baz
-
300,000-tòn lanmè Pwodiksyon k ap flote ak tankè depo (FPSO)
-
Bwat piki sekirite
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | P | S |
| RÈG GB/T | 0.05 | 1.25 | 0.50 | - | 3.00-3.75 | - | 0.03 | 0.03 |
| RÈG AWS | 0.05 | 1.25 | 0.50 | - | 3.00-3.75 | - | 0.03 | 0.03 |
| EGZANP VALÈ | 0.04 | 0.65 | 0.23 | 0.035 | 3.52 | 0.01 | 0.005 | 0.003 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | Tretman chalè °Cxh | |||||
| RÈG GB/T | 390 | 490 | 27/-100 | 20 | 605*1 | |||||
| RÈG AWS | 390 | 490 | 27/-100 | 22 | 605*1 | |||||
| EGZANP VALÈ | 460 | 550 | 61/-100 | 31 | 605*1 | |||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 2.6 * 350 | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | ||||
| ELEKTRISITE (Amp) | H/W | 80-110 | 100-130 | 130-180 | 170-210 | |||
| O/W | 60-100 | 80-120 | 120-160 | - | ||||