Low-Alloy Steels Manyèl Electrode E8016-C4 Mod jack-up rigs Consommables
Eleman prensipal la se 1.5% Ni, ki ba elektwòd men idwojèn potasyòm, nan -50C tanperati opere, severite enpak metal la depoze se ekselan.
Ki estab arc, mwens Splash, bon bòdi, fasil retire salop
Pèfòmans X-Ray se ekselan.
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Si | Mn | P | S | Ni | Cr | Mo | Lòt | |
| RÈG GB/T | 0.082 | 0.42 | 1.07 | 0.009 | 0.007 | 1.49 | 0.025 | 0.005 | - | |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | elongasyon (%) | VALÈ IMAPACT J/℃ | Tretman chalè °C*h | |||||
| RÈG GB/T | 505 | 600 | 23 | 105/-50 | 620*1 | |||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 2.6 * 350 | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | |||||
| ELEKTRISITE (Amp) | H/W | 70-100 | 100-140 | 140-180 | 180-230 | ||||
| O/W | 60-90 | 90-130 | 120-160 | - | |||||
Sanmen Nuclear Power
-
JU2000E platfòm perçage jack-up
Harbin elektrik twa pòtay CMT
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Si | Mn | P | S | Ni | Cr | Mo | Lòt | |
| RÈG GB/T | 0.082 | 0.42 | 1.07 | 0.009 | 0.007 | 1.49 | 0.025 | 0.005 | - | |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | elongasyon (%) | VALÈ IMAPACT J/℃ | Tretman chalè °C*h | |||||
| RÈG GB/T | 505 | 600 | 23 | 105/-50 | 620*1 | |||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 2.6 * 350 | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | |||||
| ELEKTRISITE (Amp) | H/W | 70-100 | 100-140 | 140-180 | 180-230 | ||||
| O/W | 60-90 | 90-130 | 120-160 | - | |||||