Ba-alyaj asye gaz ki pwoteje EG80T-G Materyèl soude
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | P | S |
| RÈG GB/T | - | - | - | - | - | - | - | - |
| RÈG AWS | - | - | - | - | - | - | - | - |
| EGZANP VALÈ | 0.06 | 1.70 | 0.3 | 0.02 | 0.8 | 0.8 | 0.01 | 0.005 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | Tretman chalè °Cxh | |||||
| RÈG GB/T | - | - | - | - | AW | |||||
| RÈG AWS | 410 | 550-700 | 27/-20 | 20 | AW | |||||
| EGZANP VALÈ | 540 | 660 | 120/-20 | 25 | AW | |||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 1.6 | ||||
| Volt | 38-42 | ||||
| Amp | 360-400 | ||||
| Longè ekstansyon sèk (mm) | 20-30 | ||||
| Koule gaz (l/min) | 25-35 | ||||
Li gen gwo vitès k ap fonn, ak arc la trè ki estab.
Sèvi ak metòd senp vètikal soude, ka trè senp pou konplete soude a.
Segondè efikasite.
-
10000TEU veso bato
-
Shandong Nikleyè pouvwa CV20
-
Guangxi Huayi esterifikasyon Tower
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | P | S |
| RÈG GB/T | - | - | - | - | - | - | - | - |
| RÈG AWS | - | - | - | - | - | - | - | - |
| EGZANP VALÈ | 0.06 | 1.70 | 0.3 | 0.02 | 0.8 | 0.8 | 0.01 | 0.005 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | Tretman chalè °Cxh | |||||
| RÈG GB/T | - | - | - | - | AW | |||||
| RÈG AWS | 410 | 550-700 | 27/-20 | 20 | AW | |||||
| EGZANP VALÈ | 540 | 660 | 120/-20 | 25 | AW | |||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 1.6 | ||||
| Volt | 38-42 | ||||
| Amp | 360-400 | ||||
| Longè ekstansyon sèk (mm) | 20-30 | ||||
| Koule gaz (l/min) | 25-35 | ||||