TIG soude fil pou asye pur ER347L soude materyèl silansye soude

YB/T5092 H022Cr20Ni10Nb

AWS A5.9ER347L

AWS A5.9M ER347L

ISO14343-A: W(19 9 Nb)

ISO14343-B: SS347L

Whatapp:+8613252436578

E-mail: sale@welding-honest.com


  • Mak:JINGLEI
  • Modèl:GTS-347L
  • Polarite ekipman pou pouvwa:DC-
  • Orijin:Lachin
  • Kostim pou:Nerjaveèi asye
  • Pozisyon soude:H/VU/F/OH
  • Gwosè:1.6mm/2.0mm/2.4mm
  • MOQ:1T Kapasite:500T pou chak mwa
  • Peman:TT, LC
  • OEM:Èske customerized
  • Pwodwi detay

    SPESIFIKASYON

    Tags pwodwi

    TIG
    A6

    TEKNOLOJI soude

    Pa kite kesyon yo
    Kontinye ante ou

    详情页-图3

    Arc enstabilite

    详情页-图2

    Bòdi disgrasyeu

    详情页-图1

    Twòp sal

    Souvan yo itilize nan machin manje, ekipman medikal, veso presyon

    Petrochemical ak lòt okazyon tankou 0Cr19Ni11Nb (SUS347L)

    01

    Ripple byen

    Akòz adisyon a nan Nb, metal la depoze gen bon
    Intergranular rezistans korozyon ak pwopriyete mekanik ki estab

    Ki estab arc, bèl fòme, bon koule nan fè fonn, ak ekselan pèfòmans pwosesis soude

    02

    Fasil salop

    Paramèt pwodwi

    KONPONÈ CHIMIK:

    ALLOY (poids%) C Mn Si P S Ni Cr Mo Lòt
    RÈG GB/T 0.025 0.39 1.71 0.02 0.01 9.21 19.62 0.13 Nb:0.37

     

    PWOPRIYETE MEKANIK:

    PWOPRIYETE FÒS RENDE (MPa) FÒS ekstansyon (MPa) elongasyon/% VALÈ IMAPACT J/℃ Tretman chalè °C*h
    RÈG GB/T - 635 39 152/-60 -

    Sipò faktori

    详情页图6
    详情页图5
    详情页图4
    详情页图3

    Pwodwi a apwopriye pou yon
    pakèt aplikasyon

    TEKNOLOJI soude

    详情页图3
    • Sichuan lwil oliv konstriksyon Lunnan baz

    详情页图2
    • Harbin Electric - Sanmen, Haiyang MSR

    详情页图1
    • 8.2 tòn transpòtè esansyèl

    KONPONÈ CHIMIK:

    ALLOY (poids%) C Mn Si P S Ni Cr Mo Lòt
    RÈG GB/T 0.025 0.39 1.71 0.02 0.01 9.21 19.62 0.13 Nb:0.37

     

    PWOPRIYETE MEKANIK:

    PWOPRIYETE FÒS RENDE (MPa) FÒS ekstansyon (MPa) elongasyon/% VALÈ IMAPACT J/℃ Tretman chalè °C*h
    RÈG GB/T - 635 39 152/-60 -