TIG soude fil pou asye pur ER312 nikleyè SG soude

YB/T5092 H12Cr30Ni9

AWS A5.9ER312

AWS A5.9M ER312

ISO14343-A: W(29 9)

ISO14343-B: SS312

Whatapp:+8613252436578

E-mail: sale@welding-honest.com


  • Mak:JINGLEI
  • Modèl:GTS-312
  • Polarite ekipman pou pouvwa:DC-
  • Orijin:Lachin
  • Kostim pou:Nerjaveèi asye
  • Pozisyon soude:H/VU/F/OH
  • Gwosè:1.6mm/2.0mm/2.4mm
  • MOQ:1T Kapasite:500T pou chak mwa
  • Peman:TT, LC
  • OEM:Èske customerized
  • Pwodwi detay

    SPESIFIKASYON

    Tags pwodwi

    TIG
    A6

    TEKNOLOJI soude

    Pa kite kesyon yo
    Kontinye ante ou

    详情页-图3

    Arc enstabilite

    详情页-图2

    Bòdi disgrasyeu

    详情页-图1

    Twòp sal

    Souvan yo itilize pou asye kabòn ak asye pur
    heterometal soude oswa tranzisyon kouch soude

    Kapab tou itilize pou ferit ak austenite disimilar jwenti ak difisil soude asye soude.

    02

    Ripple byen

    Metal la fonn gen bon rezistans dilution
    ak kontni ferit la se jiska 30%,
    ekselan rezistans tèmik krak

    Ki estab arc, bèl fòme, bon koule nan fè fonn, ak ekselan pèfòmans pwosesis soude.

    01

    Fasil salop

    Paramèt pwodwi

    KONPONÈ CHIMIK:

    ALLOY (poids%) C Mn Si P S Ni Cr Mo Lòt
    RÈG GB/T 0.019 0.5 1.71 0.022 0.003 8.42 29.86 0.11 -

     

    PWOPRIYETE MEKANIK:

    PWOPRIYETE FÒS RENDE (MPa) FÒS ekstansyon (MPa) elongasyon/% VALÈ IMAPACT J/℃ Tretman chalè °C*h
    RÈG GB/T - 815 28 - -

    Sipò faktori

    详情页图6
    详情页图5
    详情页-图10
    详情页-图9

    Pwodwi a apwopriye pou yon
    pakèt aplikasyon

    TEKNOLOJI soude

    详情页图2
    • Shandong Nikleyè pouvwa CV20

    详情页图3
    • Materyèl soude pou silansye

    详情页图3

    Hudong GNL konpayi asirans

    KONPONÈ CHIMIK:

    ALLOY (poids%) C Mn Si P S Ni Cr Mo Lòt
    RÈG GB/T 0.019 0.5 1.71 0.022 0.003 8.42 29.86 0.11 -

     

    PWOPRIYETE MEKANIK:

    PWOPRIYETE FÒS RENDE (MPa) FÒS ekstansyon (MPa) elongasyon/% VALÈ IMAPACT J/℃ Tretman chalè °C*h
    RÈG GB/T - 815 28 - -