TIG soude fil pou asye pur ER310 Sensong tank soude

YB/T5092 H11Cr26Ni21

AWS A5.9 ER310

AWS A5.9M ER310

ISO14343-A: W(25 20)

ISO14343-B: SS310

Whatapp:+8613252436578

E-mail: sale@welding-honest.com


  • Mak:JINGLEI
  • Modèl:GTS-310
  • Polarite ekipman pou pouvwa:DC-
  • Orijin:Lachin
  • Kostim pou:Nerjaveèi asye
  • Pozisyon soude:H/VU/F/OH
  • Gwosè:1.6mm/2.0mm/2.4mm
  • MOQ:1T Kapasite:500T pou chak mwa
  • Peman:TT, LC
  • OEM:Èske customerized
  • Pwodwi detay

    SPESIFIKASYON

    Tags pwodwi

    TIG
    A6

    TEKNOLOJI soude

    Pa kite kesyon yo
    Kontinye ante ou

    详情页-图3

    Arc enstabilite

    详情页-图2

    Bòdi disgrasyeu

    详情页-图1

    Twòp sal

    Souvan yo itilize nan pwodwi ki reziste tanperati ki wo
    tankou gwo founo tanperati, chabon cokéfaction
    ekipman, kapab tou itilize pou materyèl diferan soude.

    Metal la fusion gen bon pwopriyete mekanik

    05

    Ripple byen

    Ki estab rezistans tanperati ki wo, jiska 1200C

    Ki estab arc, bèl fòme, bon koule nan fè fonn, ak ekselan pèfòmans pwosesis soude.

    04

    Fasil salop

    Paramèt pwodwi

    KONPONÈ CHIMIK:

    ALLOY (poids%) C Mn Si P S Ni Cr Mo Lòt
    RÈG GB/T 0.088 0.41 1.68 0.015 0.009 20.9 25.59 0.05 -

     

    PWOPRIYETE MEKANIK:

    PWOPRIYETE FÒS RENDE (MPa) FÒS ekstansyon (MPa) elongasyon/% VALÈ IMAPACT J/℃ Tretman chalè °C*h
    RÈG GB/T - 595 36 94/-40 -

    Sipò faktori

    详情页图7
    详情页图6
    详情页图4
    详情页图3

    Pwodwi a apwopriye pou yon
    pakèt aplikasyon

    TEKNOLOJI soude

    详情页图12
    • JU2000E
      platfòm perçage jack-up

    详情页图11
    • 49,000 tòn duplex Nerjaveèi asye gaz chimik

    详情页图3
    • Materyèl soude
      pou machin tren yo

    KONPONÈ CHIMIK:

    ALLOY (poids%) C Mn Si P S Ni Cr Mo Lòt
    RÈG GB/T 0.088 0.41 1.68 0.015 0.009 20.9 25.59 0.05 -

     

    PWOPRIYETE MEKANIK:

    PWOPRIYETE FÒS RENDE (MPa) FÒS ekstansyon (MPa) elongasyon/% VALÈ IMAPACT J/℃ Tretman chalè °C*h
    RÈG GB/T - 595 36 94/-40 -