TIG soude fil pou asye pur ER309 Sekirite tank piki Consommables

YB/T5092H10Cr24Ni13

AWS A5.9ER309

AWS A5.9M ER309

ISO14343-A: W (22 12 H)

ISO14343-B: SS309

Whatapp:+8613252436578

E-mail: sale@welding-honest.com


  • Mak:JINGLEI
  • Modèl:GTS-309
  • Polarite ekipman pou pouvwa:DC-
  • Orijin:Lachin
  • Kostim pou:Nerjaveèi asye
  • Pozisyon soude:H/VU/F/OH
  • Gwosè:1.6mm/2.0mm/2.4mm
  • MOQ:1T Kapasite:500T pou chak mwa
  • Peman:TT, LC
  • OEM:Èske customerized
  • Pwodwi detay

    SPESIFIKASYON

    Tags pwodwi

    TIG
    A6

    TEKNOLOJI soude

    Pa kite kesyon yo
    Kontinye ante ou

    详情页-图3

    Arc enstabilite

    详情页-图2

    Bòdi disgrasyeu

    详情页-图1

    Twòp sal

    Souvan yo itilize pou asye kabòn ak Nerjaveèi
    asye heteromaterial soude
    oswa aplike nan pòv severite nan martensite

    Ferritik Nerjaveèi asye soude: kapab tou itilize nan pétrochimique, plant tèmik pouvwa ak lòt endistri yo.

    04

    Ripple byen

    Metal la fusion gen bon
    pwopriyete mekanik ak rezistans korozyon

    Arc ki estab, bèl fòme, bon koule nan fè fonn, ak ekselan pèfòmans pwosesis soude.

    01

    Fasil salop

    Paramèt pwodwi

    KONPONÈ CHIMIK:

    ALLOY (poids%) C Mn Si P S Ni Cr Mo Lòt
    RÈG GB/T 0.041 0.51 1.72 0.024 0.009 12.96 23.29 0.01 -

     

    PWOPRIYETE MEKANIK:

    PWOPRIYETE FÒS RENDE (MPa) FÒS ekstansyon (MPa) elongasyon/% VALÈ IMAPACT J/℃ Tretman chalè °C*h
    RÈG GB/T - 630 34 96/-40 -

    Sipò faktori

    详情页图6
    详情页-图11
    详情页图4
    详情页图3

    Pwodwi a apwopriye pou yon
    pakèt aplikasyon

    TEKNOLOJI soude

    详情页图3

    Chodyè sèvis piblik

    详情页图2

    Materyèl soude pou resipyan

    详情页图1
    • Twa pòt 2# inaktif

    KONPONÈ CHIMIK:

    ALLOY (poids%) C Mn Si P S Ni Cr Mo Lòt
    RÈG GB/T 0.041 0.51 1.72 0.024 0.009 12.96 23.29 0.01 -

     

    PWOPRIYETE MEKANIK:

    PWOPRIYETE FÒS RENDE (MPa) FÒS ekstansyon (MPa) elongasyon/% VALÈ IMAPACT J/℃ Tretman chalè °C*h
    RÈG GB/T - 630 34 96/-40 -