Nerjaveèi SAW soude fil ER308L ak flux Soudi bagay
TEKNOLOJI soude
Pa kite kesyon yo
Kontinye ante ou
Arc enstabilite
Bòdi disgrasyeu
Twòp sal
Lajman itilize nan petwochimik, veso presyon
Machin manje, ekipman medikal ak lòt endistri ki gen rapò.
Ripple byen
Ba kabòn 18% Cr-8% Ni Nerjaveèi (SUS304) pou soude
Bon soudabilite, sansiblite rezistans krak.
Fasil salop
Paramèt pwodwi
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Si | Mn | P | S | Ni | Cr | Mo |
RÈG GB/T | 0.016 | 0.8 | 1.64 | 0.025 | 0.002 | 9.75 | 19.53 | - |
PWOPRIYETE MEKANIK:
PWOPRIYETE | Fòs ekstansyon (Mpa) | elongasyon/% | VALÈ IMAPACT J/℃ | Kowozyon entègranulèr | ||||
RÈG GB/T | 570 | 38 | ≥31/-196 | GB/T4334E metòd te pase |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 2.4 | 3.2 | 4.0 | ||||
Volt | 28-32 | 28-32 | 28-32 | ||||
Amp | 270-360 | 400-550 | 500-650 | ||||
Vitès (mm/min) | 250-320 | 300-420 | 400-480 | ||||
elongasyon sèk (mm) | 20-24 | 22-26 | 30-34 |
Sipò faktori
Pwodwi a apwopriye pou yon
pakèt aplikasyon
TEKNOLOJI soude
-
Réacteurs polypropylène
-
Sichuan lwil oliv konstriksyon Lunnan baz
-
Shanghai Morimatsu tank depo
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Si | Mn | P | S | Ni | Cr | Mo |
RÈG GB/T | 0.016 | 0.8 | 1.64 | 0.025 | 0.002 | 9.75 | 19.53 | - |
PWOPRIYETE MEKANIK:
PWOPRIYETE | Fòs ekstansyon (Mpa) | elongasyon/% | VALÈ IMAPACT J/℃ | Kowozyon entègranulèr | ||||
RÈG GB/T | 570 | 38 | ≥31/-196 | GB/T4334E metòd te pase |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 2.4 | 3.2 | 4.0 | ||||
Volt | 28-32 | 28-32 | 28-32 | ||||
Amp | 270-360 | 400-550 | 500-650 | ||||
Vitès (mm/min) | 250-320 | 300-420 | 400-480 | ||||
elongasyon sèk (mm) | 20-24 | 22-26 | 30-34 |