Nerjaveèi asye MIG H09Cr21Ni9Mn7Si Materyèl soude
Aplikasyon
Apwopriye pou plak asye bal, soumaren nikleyè ak lòt pa bezwen okazyon mayetik, kapab tou itilize pou difisil soude ak fasil krak soude asye diferan.
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu | |
RÈG GB/T | 0.04-0.14 | 6.5-8.0 | 0.65-1.0 | 18.5-22.0 | 8.0-10.7 | 0.75 | 0.03 | 0.03 | 0.75 | |
RÈG AWS | - | - | - | - | - | - | - | - | - | |
EGZANP VALÈ | 0.071 | 6.73 | 0.7 | 18.83 | 8.96 | 0.01 | 0.014 | 0.012 | 0.01 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
RÈG GB/T | - | - | - | - | ||||
RÈG AWS | - | - | - | - | ||||
EGZANP VALÈ | - | 630 | - | 39 |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 0.8 | 1.0 | 1.2 | ||||
ELEKTRISITE (Amp) | H/W | 70-150 | 100-200 | 140-220 | |||
O/W | 50-120 | 80-150 | 120-180 |
Espesyalite
Eleman prensipal la se 18% Cr-8% Ni-6% Mn.
Lis fil manje, arc ki estab, bèl fòme, bon koule nan fè fonn, mwens Splash, ak ekselan pèfòmans pwosesis soude.
Metal fonn gen bon pwopriyete mekanik.
Montre detay
Estabilite nan arc
Bèl fòm
Sou nou
Ekspozisyon fioor faktori
Ka aplikasyon an
Harbin elektrik twa pòt CMT
Tangshan LNG ekspòtasyon tiyo pwojè
Tire reyèl faktori
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu | |
RÈG GB/T | 0.04-0.14 | 6.5-8.0 | 0.65-1.0 | 18.5-22.0 | 8.0-10.7 | 0.75 | 0.03 | 0.03 | 0.75 | |
RÈG AWS | - | - | - | - | - | - | - | - | - | |
EGZANP VALÈ | 0.071 | 6.73 | 0.7 | 18.83 | 8.96 | 0.01 | 0.014 | 0.012 | 0.01 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
RÈG GB/T | - | - | - | - | ||||
RÈG AWS | - | - | - | - | ||||
EGZANP VALÈ | - | 630 | - | 39 |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 0.8 | 1.0 | 1.2 | ||||
ELEKTRISITE (Amp) | H/W | 70-150 | 100-200 | 140-220 | |||
O/W | 50-120 | 80-150 | 120-180 |