Sitou itilize nan lanmè lwil oliv ak gaz, pwodui chimik, petwòl ak endistri pétrochimique nan sistèm tiyo a, liy koule soude nan rize, kolekte tiyo, elatriye.
Apwopriye pou soude duplex asye pur ki gen 25% Cr,
tankou 00 cr25ni7mo4n, 03 cr25ni6mo3cu2n, UNS 32550 (Alloy255), elatriye.
Ripple byen
Low idwojèn super duplex Nerjaveèi men elektwòd, konpozisyon prensipal la se 25Cr-9.5Ni-3.4Mo-2.5Cu-0.2N
Metal la soude se estrikti bifaz austenitic ak feritik, ak endèks rezistans korozyon an se PRE> 40. Li gen gwo fòs ak bon rezistans nan pitting ak krak korozyon estrès. Ekselan teknoloji soude, arc ki estab, bèl fòme, rid delika, ti Splash, fasil retire salop.
Fasil salop
Paramèt pwodwi
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | Lòt |
RÈG GB/T | 0.03 | 1.02 | 0.46 | 0.016 | 0.011 | 9.1 | 24.5 | 3.1 | 1.91 | N: 0.17 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | Tretman chalè °C*h | ||||
RÈG GB/T | 905 | 24 | - | - |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 2.0 * 250 | 2.6 * 300 | 3.2 * 350 | 4.0 * 350 | 5.0 * 350 | |||||
ELEKTRISITE (Amp) | H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |
Sipò faktori
Pwodwi a apwopriye pou yon
pakèt aplikasyon
TEKNOLOJI soude
-
Lachin-Larisi devan lès
-
Shandong Nikleyè pouvwa CV20
-
JU2000E platfòm perçage jack-up
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | Lòt |
RÈG GB/T | 0.031 | 1.15 | 0.45 | 0.023 | 0.01 | 8.3 | 24.1 | 2.92 | 1.94 | N: 0.15 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | Tretman chalè °C*h | ||||
RÈG GB/T | 885 | 22 | - | - |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 2.0 * 250 | 2.6 * 300 | 3.2 * 350 | 4.0 * 350 | 5.0 * 350 | |||||
ELEKTRISITE (Amp) | H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |