Apwopriye pou soude nan doub faz asye pur
00Cr22Ni5Mo3N (SUS2205) nan endistri pétrochimique.
Pot asid kalite Nerjaveèi men elektwòd, jè arc, eleman prensipal la se 22%Cr-9%Ni-3%Mo-N.
Ripple byen
Weld metal gen apeprè 50% ferit, tou de austenite ak
pwopriyete ferit, ak fòs segondè, ekselan rezistans korozyon estrès;
Ekselan teknoloji soude, arc ki estab, bèl fòme, rid delika, ti Splash, fasil retire salop.
Fasil salop
Paramèt pwodwi
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | Lòt |
| RÈG GB/T | 0.028 | 0.82 | 0.74 | 0.026 | 0.008 | 9.04 | 24.4 | 3.45 | 0.02 | N: 0.15 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | Tretman chalè °C*h | ||||
| RÈG GB/T | 860 | 26 | - | - | ||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 2.0 * 250 | 2.6 * 300 | 3.2 * 350 | 4.0 * 350 | 5.0 * 350 | |||||
| ELEKTRISITE (Amp) | H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
| O/W | 20-50 | 45-80 | 70-110 | 90-135 | - | |||||
Sipò faktori
Pwodwi a apwopriye pou yon
pakèt aplikasyon
TEKNOLOJI soude
-
3,000 mèt dlo fon semi-
platfòm perçage submersible "
Haiyang Shiyou 981"
-
Hengli Petrochemical
20 milyon tònn/ane raffinage
ak pwojè entegrasyon chimik
-
Nankin Chengzhi Yongqing
Enèji 07MnNiMoDR
tank vinil boul asye
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | Lòt |
| RÈG GB/T | 0.028 | 0.82 | 0.74 | 0.026 | 0.008 | 9.04 | 24.4 | 3.45 | 0.02 | N: 0.15 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | Tretman chalè °C*h | ||||
| RÈG GB/T | 860 | 26 | - | - | ||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 2.0 * 250 | 2.6 * 300 | 3.2 * 350 | 4.0 * 350 | 5.0 * 350 | |||||
| ELEKTRISITE (Amp) | H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
| O/W | 20-50 | 45-80 | 70-110 | 90-135 | - | |||||