Nerjaveèi asye Flux Cored Fil EGT1-4 Reactor konpozan soude
TEKNOLOJI soude
Pa kite kesyon yo
Kontinye ante ou
Arc enstabilite
Bòdi disgrasyeu
Twòp sal
Apwopriye pou soude SUS316Nb ak 316Ti
Anplis de sa nan Nb ka efektivman amelyore rezistans nan korozyon intergranular
Ripple byen
Arc la se mou ak ki estab, mwens Splash, bèl fòme
Bon retire salop, manje fil ki estab, ak ekselan pèfòmans pwosesis soude.
Fasil salop
Paramèt pwodwi
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | P | S | Ni | Cr | Mo | Lòt |
RÈG GB/T | 0.02 | 0.6 | 1.50 | 0.02 | 0.003 | 12 | 19.5 | 2.5 | Nb:0.25 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | elongasyon/% | VALÈ IMAPACT J/℃ | Tretman chalè °C*h | |||||
RÈG GB/T | - | 650 | 35 | - | - |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 1.2 | 1.6 | |||
Voltage (Vòlt) | 22-36 | 26-38 | |||
Elektrisite (Amp) | 120-260 | 200-300 | |||
Vitès (mm/min) | 15-20 | 18-25 | |||
Longè detire sèk (mm) | 15-25 | 15-25 |
Sipò faktori
Pwodwi a apwopriye pou yon
pakèt aplikasyon
TEKNOLOJI soude
Entèn raktor
-
981 semi-submersible forage mare
-
8.2-tòn transpòtè esansyèl
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | P | S | Ni | Cr | Mo | Lòt |
RÈG GB/T | 0.02 | 0.6 | 1.50 | 0.02 | 0.003 | 12 | 19.5 | 2.5 | Nb:0.25 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | elongasyon/% | VALÈ IMAPACT J/℃ | Tretman chalè °C*h | |||||
RÈG GB/T | - | 650 | 35 | - | - |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 1.2 | 1.6 | |||
Voltage (Vòlt) | 22-36 | 26-38 | |||
Elektrisite (Amp) | 120-260 | 200-300 | |||
Vitès (mm/min) | 15-20 | 18-25 | |||
Longè detire sèk (mm) | 15-25 | 15-25 |