Nerjaveèi asye Flux Cored Fil EGT1-1 LNG machin boutèy materyèl soude
TEKNOLOJI soude
Pa kite kesyon yo
Kontinye ante ou
Arc enstabilite
Bòdi disgrasyeu
Twòp sal
Ekselan pèfòmans pwosesis soude
Konpozisyon prensipal la se 20% Cr-25% Ni-5% Mo-2% Cu
Ripple byen
Ekselan rezistans korozyon, ka reziste
asid silfirik, asid fosfò inifòm korozyon
Apwopriye pou chak gwoup gwo fò won asid, tank, tiyo ak soude veso depo, tankou 904L.
Fasil salop
Paramèt pwodwi
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu | |
RÈG GB/T | - | - | - | - | - | - | - | - | - | |
RÈG AWS | - | - | - | - | - | - | - | - | - | |
EGZANP VALÈ | 0.025 | 1.1 | 0.6 | 21 | 25.5 | 4.5 | 0.2 | 0.030 | 1.50 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
RÈG GB/T | - | - | - | - | ||||
RÈG AWS | - | - | - | - | ||||
EGZANP VALÈ | - | 620 | - | 39 |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 1.2 | 1.6 | ||||||
Volt | 22-36 | 26-38 | ||||||
Amp | 120-260 | 200-300 | ||||||
Longè ekstansyon sèk (mm) | 15-20 | 18-25 | ||||||
Koule gaz (l/min) | 15-25 | 15-25 |
Sipò faktori
Pwodwi a apwopriye pou yon
pakèt aplikasyon
TEKNOLOJI soude
Guangxi Huayi
methanol dezidratasyon gwo kay won
Zhenhai rafine pwojè
1 milyon tònn/ane etilèn
Sichuan lwil oliv
konstriksyon baz Lunnan
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu | |
RÈG GB/T | - | - | - | - | - | - | - | - | - | |
RÈG AWS | - | - | - | - | - | - | - | - | - | |
EGZANP VALÈ | 0.025 | 1.1 | 0.6 | 21 | 25.5 | 4.5 | 0.2 | 0.030 | 1.50 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | ||||
RÈG GB/T | - | - | - | - | ||||
RÈG AWS | - | - | - | - | ||||
EGZANP VALÈ | - | 620 | - | 39 |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 1.2 | 1.6 | ||||||
Volt | 22-36 | 26-38 | ||||||
Amp | 120-260 | 200-300 | ||||||
Longè ekstansyon sèk (mm) | 15-20 | 18-25 | ||||||
Koule gaz (l/min) | 15-25 | 15-25 |