Nerjaveèi asye Flux Cored Fil E308HT1-1 Sensong tank soude
TEKNOLOJI soude
Pa kite kesyon yo
Kontinye ante ou
Arc enstabilite
Bòdi disgrasyeu
Twòp sal
Apwopriye pou petwochimik, presyon
veso, machin manje, machin medikal
Angrè chimik ak lòt endistri ki gen rapò, soude 18% Cr-8% Ni Nerjaveèi (SUS304, 304L, elatriye).
Ripple byen
Paske li gen yon sèten kantite kabòn, li seapwopriye
pou soude ekipman asye pur itilize nan tanperati ki wo
Ba fusion pwen Bi eleman kontwòl trè ba, sansiblite cho krak soudure metal nan anwo nan syèl la
se anviwònman tanperati redwi, arc la se mou ak ki estab, spatter a se mwens, bòdi a
se bèl, retire salop la bon, fil manje a ki estab, gen ekselan pèfòmans pwosesis soude.
Fasil salop
Paramèt pwodwi
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | P | S | Ni | Cr | Mo | Lòt |
| RÈG GB/T | 0.05 | 0.65 | 1.30 | 0.02 | 0.005 | 9.8 | 19.5 | 0.01 | Bi:0.0005 |
PWOPRIYETE MEKANIKA:、
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | elongasyon/% | VALÈ IMAPACT J/℃ | Tretman chalè °C*h | |||||
| RÈG GB/T | - | 600 | 40 | - | - | |||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 1.2 | 1.6 | |||
| Voltage (Vòlt) | 22-36 | 26-38 | |||
| Elektrisite (Amp) | 120-260 | 200-300 | |||
| Vitès (mm/min) | 15-20 | 18-25 | |||
| Longè detire sèk (mm) | 15-25 | 15-25 |
Sipò faktori
Pwodwi a apwopriye pou yon
pakèt aplikasyon
TEKNOLOJI soude
-
Materyèl soude pou machin tren yo
Harbin elektrik twa pòtay CMT
-
CJ50 jack-up egzèsis
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | P | S | Ni | Cr | Mo | Lòt |
| RÈG GB/T | 0.05 | 0.65 | 1.30 | 0.02 | 0.005 | 9.8 | 19.5 | 0.01 | Bi:0.0005 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | elongasyon/% | VALÈ IMAPACT J/℃ | Tretman chalè °C*h | |||||
| RÈG GB/T | - | 600 | 40 | - | - | |||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 1.2 | 1.6 | |||
| Voltage (Vòlt) | 22-36 | 26-38 | |||
| Elektrisite (Amp) | 120-260 | 200-300 | |||
| Vitès (mm/min) | 15-20 | 18-25 | |||
| Longè detire sèk (mm) | 15-25 | 15-25 |