、Low-alyaj asye Manyèl elektwòd E8018-C1 soude fabwikasyon makings
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Ni | Cr | Mo | P | S |
RÈG GB/T | 0.12 | 1.25 | 0.80 | 2.00-2.75 | - | - | 0.03 | 0.03 |
RÈG AWS | 0.12 | 1.25 | 0.80 | 2.00-2.75 | - | - | 0.03 | 0.03 |
EGZANP VALÈ | 0.055 | 0.85 | 0.32 | 2.2 | 0.023 | 0.11 | 0.007 | 0.006 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | Tretman chalè °Cxh | |||||
RÈG GB/T | 460 | 550 | 27/-60 | 17 | 605*1 | |||||
RÈG AWS | 460 | 550 | 27/-60 | 19 | 605*1 | |||||
EGZANP VALÈ | 475 | 580 | 95/-60 | 26 | 605*1 |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 2.6 * 350 | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | ||||
ELEKTRISITE (Amp) | H/W | 80-110 | 100-130 | 130-180 | 170-210 | |||
O/W | 60-100 | 80-120 | 120-160 | - |
Iron poud ba idwojèn potasyòm kalite men elektwòd.
Akòz adisyon nan poud fè, efikasite k ap fonn se pi wo, severite enpak metal la fonn nan tanperati k ap travay -60 ℃ ekselan.
Ki estab arc, mwens Splash, bon fòme, fasil retire salop, pèfòmans X-Ray se ekselan.
Chodyè sèvis piblik
9,000 tòn pwodwi chimik yo
Plant Nikleyè Sanmen
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Ni | Cr | Mo | P | S |
RÈG GB/T | 0.12 | 1.25 | 0.80 | 2.00-2.75 | - | - | 0.03 | 0.03 |
RÈG AWS | 0.12 | 1.25 | 0.80 | 2.00-2.75 | - | - | 0.03 | 0.03 |
EGZANP VALÈ | 0.055 | 0.85 | 0.32 | 2.2 | 0.023 | 0.11 | 0.007 | 0.006 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | Tretman chalè °Cxh | |||||
RÈG GB/T | 460 | 550 | 27/-60 | 17 | 605*1 | |||||
RÈG AWS | 460 | 550 | 27/-60 | 19 | 605*1 | |||||
EGZANP VALÈ | 475 | 580 | 95/-60 | 26 | 605*1 |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 2.6 * 350 | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | ||||
ELEKTRISITE (Amp) | H/W | 80-110 | 100-130 | 130-180 | 170-210 | |||
O/W | 60-100 | 80-120 | 120-160 | - |