Ba-alyaj asye Manyèl elektwòd E7018-B2L metal Jointing makings
Iron poud ba idwojèn potasyòm kalite men soude baton, ki estab arc
Mwens Splash, bon bòdi, fasil yo retire salop X-Ray pèfòmans
Pwopriyete mekanik ki estab, severite enpak segondè ka kenbe anba kondisyon tretman chalè
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Si | Mn | P | S | Ni | Cr | Mo | Lòt |
| RÈG GB/T | 0.04 | 0.35 | 0.8 | 0.013 | 0.01 | 0.018 | 1.28 | 0.51 | - |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | elongasyon (%) | VALÈ IMAPACT J/℃ | Tretman chalè °C*h | |||||
| RÈG GB/T | 455 | 560 | 23 | 175/Nòmal tanperati | 690*1 | |||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | ||||
| ELEKTRISITE (Amp) | H/W | 90-130 | 140-190 | 190-240 | |||
| O/W | 80-120 | 120-160 | - | ||||
-
Sino-Ris devan lès
Plant Nikleyè Haiyang
-
400,000 tòn transpòtè minrè
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Si | Mn | P | S | Ni | Cr | Mo | Lòt |
| RÈG GB/T | 0.04 | 0.35 | 0.8 | 0.013 | 0.01 | 0.018 | 1.28 | 0.51 | - |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | elongasyon (%) | VALÈ IMAPACT J/℃ | Tretman chalè °C*h | |||||
| RÈG GB/T | 455 | 560 | 23 | 175/Nòmal tanperati | 690*1 | |||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | ||||
| ELEKTRISITE (Amp) | H/W | 90-130 | 140-190 | 190-240 | |||
| O/W | 80-120 | 120-160 | - | ||||