Low-Alloy Steels Manyèl Electrode E7016-C2L Reactor konpozan soude
Konpozisyon prensipal la se 3.5% Ni asye, ki ba idwojèn potasyòm kalite men soude baton, nan -75C tanperati opere, k ap fonn li yo.
Severite enpak metal la ekselan.
Ki estab arc, mwens Splash, bon bòdi, fasil retire salop, pèfòmans X-Rav se ekselan.
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Si | Mn | P | S | Ni | Cr | Mo | Lòt | |
| RÈG GB/T | 0.038 | 0.19 | 0.64 | 0.006 | 0.004 | 3.56 | 0.033 | 0.8 | - | |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | elongasyon (%) | VALÈ IMAPACT J/℃ | Tretman chalè °C*h | |||||
| RÈG GB/T | 475 | 550 | 28 | 65/-100 | 620*1 | |||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 2.6 * 350 | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | |||||
| ELEKTRISITE (Amp) | H/W | 70-100 | 100-140 | 140-180 | 180-230 | ||||
| O/W | 60-90 | 90-130 | 120-160 | - | |||||
Entèn raktor
-
Qinghai Youjian Wunan lwil oliv
-
308,000 tòn VLCC lwil brit bato
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Si | Mn | P | S | Ni | Cr | Mo | Lòt | |
| RÈG GB/T | 0.038 | 0.19 | 0.64 | 0.006 | 0.004 | 3.56 | 0.033 | 0.8 | - | |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | elongasyon (%) | VALÈ IMAPACT J/℃ | Tretman chalè °C*h | |||||
| RÈG GB/T | 475 | 550 | 28 | 65/-100 | 620*1 | |||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 2.6 * 350 | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | |||||
| ELEKTRISITE (Amp) | H/W | 70-100 | 100-140 | 140-180 | 180-230 | ||||
| O/W | 60-90 | 90-130 | 120-160 | - | |||||