Ba-alyaj asye Manyèl elektwòd E7016-B2L metal Jointing koneksyon
Iron poud ba idwojèn potasyòm kalite men soude baton, ki estab arc
Mwens Splash, bon bòdi, fasil yo retire salop X-Ray pèfòmans
Pwopriyete mekanik ki estab, severite enpak segondè ka kenbe anba kondisyon tretman chalè
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Si | Mn | P | S | Ni | Cr | Mo | Lòt |
| RÈG GB/T | 0.037 | 0.28 | 0.82 | 0.011 | 0.008 | 0.012 | 1.21 | 0.48 | - |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | elongasyon (%) | VALÈ IMAPACT J/℃ | Tretman chalè °C*h | |||||
| RÈG GB/T | 480 | 575 | 24 | 170/Nòmal tanperati | 690*1 | |||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | ||||
| ELEKTRISITE (Amp) | H/W | 90-130 | 140-190 | 190-240 | |||
| O/W | 80-120 | 120-160 | - | ||||
-
Mei Jin Hua Sheng
glycol sentetik gwo kay won
-
Hainan Huasheng
gwo kay won rekiperasyon fenol
-
GDS-2209/GXS-E330
tib sifas soude sit
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Si | Mn | P | S | Ni | Cr | Mo | Lòt |
| RÈG GB/T | 0.037 | 0.28 | 0.82 | 0.011 | 0.008 | 0.012 | 1.21 | 0.48 | - |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | elongasyon (%) | VALÈ IMAPACT J/℃ | Tretman chalè °C*h | |||||
| RÈG GB/T | 480 | 575 | 24 | 170/Nòmal tanperati | 690*1 | |||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | ||||
| ELEKTRISITE (Amp) | H/W | 90-130 | 140-190 | 190-240 | |||
| O/W | 80-120 | 120-160 | - | ||||