Ba-alyaj asye Manyèl elektwòd E7015-C1L Joint soude
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | P | S |
RÈG GB/T | 0.12 | 1.25 | 0.60 | - | 2.0-2.75 | - | 0.03 | 0.03 |
RÈG AWS | 0.05 | 1.25 | 0.50 | - | 2.0-2.75 | - | 0.03 | 0.03 |
EGZANP VALÈ | 0.04 | 0.65 | 0.2 | 0.018 | 2.56 | 0.06 | 0.007 | 0.006 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | Tretman chalè °Cxh | |||||
RÈG GB/T | 390 | 490 | 27/-75 | 20 | 605*1 | |||||
RÈG AWS | 390 | 490 | 27/-75 | 22 | 605*1 | |||||
EGZANP VALÈ | 410 | 520 | 105/-75 | 26 | 605*1 |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 2.6 * 350 | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | ||||
ELEKTRISITE (Amp) | H/W | 80-110 | 100-130 | 130-180 | 170-210 | |||
O/W | 60-100 | 80-120 | 120-160 | - |
Konpozisyon prensipal la se 2.5% Ni asye.
Po dwòg ki ba idwojèn potasyòm, CLADDING an metal nan -75 ° C gen severite enpak ekselan.
Ki estab arc, mwens Splash, bon fòme, fasil retire salop, pèfòmans X-Ray se ekselan.
180,000 tòn Capesize en
Shanghai Morimatsu Depo tank
Réacteurs polypropylène
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | P | S |
RÈG GB/T | 0.12 | 1.25 | 0.60 | - | 2.0-2.75 | - | 0.03 | 0.03 |
RÈG AWS | 0.05 | 1.25 | 0.50 | - | 2.0-2.75 | - | 0.03 | 0.03 |
EGZANP VALÈ | 0.04 | 0.65 | 0.2 | 0.018 | 2.56 | 0.06 | 0.007 | 0.006 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | VALÈ IMAPACT J/℃ | ELONGATION (%) | Tretman chalè °Cxh | |||||
RÈG GB/T | 390 | 490 | 27/-75 | 20 | 605*1 | |||||
RÈG AWS | 390 | 490 | 27/-75 | 22 | 605*1 | |||||
EGZANP VALÈ | 410 | 520 | 105/-75 | 26 | 605*1 |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 2.6 * 350 | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | ||||
ELEKTRISITE (Amp) | H/W | 80-110 | 100-130 | 130-180 | 170-210 | |||
O/W | 60-100 | 80-120 | 120-160 | - |