AWS E7015-A1 Ba-alyaj asye Manyèl elektwòd Soudi Pwodwi pou Telefòn
GER-107 (R107) men elektwòd pou chalè reziste asye, Jinglei R107 chalè rezistan elektwòd asye GB estanda se E5015-1M3 P, apwopriye pou soude tanperati k ap travay nan tiyo sa a 510 degre chodyè, echanjeur chalè ak lòt okazyon, tankou ASTM A204. ak A335-P1 tiyo;
Atik soude: 1. Prechofaj ak tanperati kanal (kouch): 90-110 ℃; 2. Tretman chalè: selon kondisyon estanda materyèl soude yo, se tretman chalè te pote soti nan 620±15℃x1h.
Aplikasyon & Estanda & Nòt:
E7015 kalite ba alyaj asye men elektwòd se apwopriye pou soude tanperati k ap travay anba a 510 ℃ tiyo chodyè, echanjeur chalè ak lòt okazyon, tankou ASTM A204 ak A335-P1 tiyo;
Elektwòd la dwe cheche anvan ou itilize, kenbe yon arc kout, itilize nan bak metòd soude pi devan, evite ensidan an nan porosite nan arc la; Yo ta dwe konsève ba idwojèn pandan tout pwosesis la soude. Low alyaj sele elektwòd asye, anjeneral dapre konpozisyon chimik nan asye, pwopriyete mekanik, rezistans krak ak lòt kondisyon, men tou, soti nan fòm nan estrikti soude, kondisyon travay, estrès ak ekipman soude ak lòt aspè nan konsiderasyon konplè. Si sa nesesè, yo dwe fè tès pèfòmans soude pou detèmine elektwòd la epi yo dwe pran mezi pwosesis ki nesesè yo.
Karakteristik
1. Elektwòd idwojèn sodyòm ki ba, ajoute 0.5% Mo pou amelyore fòs soude ak rezistans korozyon;
2. Ki estab arc, mwens Splash, bon fòme, fasil dezagger, pèfòmans X-Ray se ekselan.
Anjeneral chwazi elektwòd ki koresponn lan dapre fòs nan klas asye a, an menm tan an tou bezwen soudabilite asye, tranzisyon an nan eleman metal paran, bay gabèl reponn gwosè a estrikti, fòm, Groove ak faktè konsantrasyon estrès, tankou konplè. konsiderasyon, vitès la refwadisman nan soude se twò gwo, se yon fòs ki pi wo, soude pwodwi lari fasil krak sikonstans yo negatif, souvan ka chwazi kèk mwens pase fòs la nan elektwòd metal paran.
Konpayi & faktori
Konpozisyon pwodwi ak pwopriyete mekanik entwodiksyon
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Cr | Mo | P | S |
| RÈG GB/T | 0.12 | 1.00 | 0.80 | - | 0.40-0.65 | 0.03 | 0.030 |
| RÈG AWS | 0.12 | 0.90 | 0.60 | - | 0.40-0.65 | 0.03 | 0.030 |
| EGZANP VALÈ | 0.07 | 0.75 | 0.35 | 0.035 | 0.55 | 0.014 | 0.012 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | CHALÈ℃xh | VALÈ IMAPACT J/℃ | ELONGATION (%) | |||||||||
| RÈG GB/T | 390 | 490 | 620*1 | - | 22 | |||||||||
| RÈG AWS | 390 | 490 | 620*1 | - | 22 | |||||||||
| EGZANP VALÈ | 477 | 570 | 620*1 | 150/Nòmal tanperati | 28 | |||||||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 2.6 * 350 | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | ||||||
| ELEKTRISITE (Amp) | H/W | 80-110 | 100-130 | 130-180 | 170-210 | |||||
| O/W | 60-100 | 80-120 | 120-160 | - | ||||||
Detay anbalaj:
| 2.6mm | 300mm | 48PCS | 2KG | |||
| 3.2mm | 350mm | 27PCS | 5KG | |||
| 4.0mm | 350mm | 16PCS | 5KG | |||
| 5.0mm | 350mm | 12PCS | 5KG | |||
Ka tipik
Sètifika
Konpozisyon pwodwi ak pwopriyete mekanik entwodiksyon
KONPONÈ CHIMIK:
| ALLOY (poids%) | C | Mn | Si | Cr | Mo | P | S |
| RÈG GB/T | 0.12 | 1.00 | 0.80 | - | 0.40-0.65 | 0.03 | 0.030 |
| RÈG AWS | 0.12 | 0.90 | 0.60 | - | 0.40-0.65 | 0.03 | 0.030 |
| EGZANP VALÈ | 0.07 | 0.75 | 0.35 | 0.035 | 0.55 | 0.014 | 0.012 |
PWOPRIYETE MEKANIK:
| PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | CHALÈ℃xh | VALÈ IMAPACT J/℃ | ELONGATION (%) | |||||||||
| RÈG GB/T | 390 | 490 | 620*1 | - | 22 | |||||||||
| RÈG AWS | 390 | 490 | 620*1 | - | 22 | |||||||||
| EGZANP VALÈ | 477 | 570 | 620*1 | 150/Nòmal tanperati | 28 | |||||||||
PARAMÈT SOUDE REKÒMANDE:
| DYAMET SPECIFICATIONS (mm) | 2.6 * 350 | 3.2 * 350 | 4.0 * 400 | 5.0 * 400 | ||||||
| ELEKTRISITE (Amp) | H/W | 80-110 | 100-130 | 130-180 | 170-210 | |||||
| O/W | 60-100 | 80-120 | 120-160 | - | ||||||
Detay anbalaj:
| 2.6mm | 300mm | 48PCS | 2KG | |||
| 3.2mm | 350mm | 27PCS | 5KG | |||
| 4.0mm | 350mm | 16PCS | 5KG | |||
| 5.0mm | 350mm | 12PCS | 5KG | |||