AWS E309MoL Nerjaveèi asye manyèl elektwòd soude done fabwikasyon
Aplikasyon & Estanda & Nòt:
1. fèt nan Kiba pou fe en ak kabòn STEEL OSWA BAS ALLOY fe disimilar STEEL SOULD, en fe afich plak blanch soudure, 316 SERIES en fe sifas soudure sou kabòn fe oubyen ba alyaj fe.
2. estanda nou te rankontre: GB/T983 E309LMo-16, AWS A5.4 E309LMo-16 & A5.4M E309LMo-16, ISO3581-A:E(23 12 2 L) R 1 2, ISO3581-B:ES309LMo- 16
Kontwòl pwosesis soude:
Ba vòltaj arc soude; Balanse elektwòd la pa ka twò lajè, jeneralman nan 3 fwa dyamèt elektwòd la; Vitès soude pa ka twò dousman, nan ka ta gen surchof ak salop, men nan ka fasil fann, chwazi ki ba aktyèl soude dousman. Vètikal soude akòz karakteristik sa yo nan dlo asye pur se fasil koule, chwa ki pi bon se sèvi ak kase soude arc. Multi-kouch soude dwe netwaye salop soude. Piyo a arc dwe ranpli lè arc la fèmen.
Karakteristik
1. Titàn kalsyòm Nerjaveèi elektwòd, konpozisyon prensipal la se 22% CR-12%Ni-2%Mo
2. Arc ki estab, bèl fòme, rid amann, kèk pwojeksyon, fasil de-slagging, bon rezistans dife nan po dwòg, bon rezistans stomatik.
3. Metal la soude gen plis ferit, akòz ajoute Mo, li gen sansiblite krak ki ba.
Titàn kalsyòm kalite ultra-ba kabòn Cr23Ni13Mo2Cu Nerjaveèi elektwòd, AC ak DC itilizasyon doub, soude a ak kantite lajan an dwa nan molybdène, amelyore soude metal krak rezistans a ak rezistans korozyon. Itilize pou menm kalite kabòn ultra-ba asye pur ak asye diferan.
Konpayi & faktori
Konpozisyon pwodwi ak pwopriyete mekanik entwodiksyon
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
RÈG GB/T | 0.04 | 0.5-2.5 | 1.00 | 22.0-25.0 | 12.0-14.0 | 2.0-3.0 | 0.040 | 0.03 | 0.75 |
RÈG AWS | 0.04 | 0.5-2.5 | 1.00 | 22.0-25.0 | 12.0-14.0 | 2.0-3.0 | 0.040 | 0.03 | 0.75 |
EGZANP VALÈ | 0.028 | 1.43 | 0.77 | 23.2 | 13.1 | 2.5 | 0.027 | 0.006 | 0.1 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | CHALÈ℃xh | VALÈ IMAPACT J/℃ | ELONGATION (%) | |||||||||
RÈG GB/T | - | 510 | - | - | 25 | |||||||||
RÈG AWS | - | 520 | - | - | 30 | |||||||||
EGZANP VALÈ | - | 660 | - | - | 34 |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 2.0 * 250 | 2.6 * 300 | 3.2 * 350 | 4.0 * 350 | 5.0 * 350 | |||||||
ELEKTRISITE (Amp) | H/W | 50-75 | 70-95 | 80-120 | 110-160 | 160-190 | ||||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |
Detay anbalaj:
SEPSIFIKASYON | LONGÈ | PCS/1KG | PWA/1KG | |||
2.0mm | 300mm | 79PCS | 2KG | |||
2.6mm | 300mm | 48PCS | 2KG | |||
3.2mm | 350mm | 27PCS | 5KG | |||
4.0mm | 350mm | 16PCS | 5KG | |||
5.0mm | 350mm | 12PCS | 5KG |
REMAK:
H/W: pozisyon orizontal soude
O/W: soude pozisyon sou tèt
Ka tipik
Sètifika
Konpozisyon pwodwi ak pwopriyete mekanik entwodiksyon
KONPONÈ CHIMIK:
ALLOY (poids%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
RÈG GB/T | 0.04 | 0.5-2.5 | 1.00 | 22.0-25.0 | 12.0-14.0 | 2.0-3.0 | 0.040 | 0.03 | 0.75 |
RÈG AWS | 0.04 | 0.5-2.5 | 1.00 | 22.0-25.0 | 12.0-14.0 | 2.0-3.0 | 0.040 | 0.03 | 0.75 |
EGZANP VALÈ | 0.028 | 1.43 | 0.77 | 23.2 | 13.1 | 2.5 | 0.027 | 0.006 | 0.1 |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | CHALÈ℃xh | VALÈ IMAPACT J/℃ | ELONGATION (%) | |||||||||
RÈG GB/T | - | 510 | - | - | 25 | |||||||||
RÈG AWS | - | 520 | - | - | 30 | |||||||||
EGZANP VALÈ | - | 660 | - | - | 34 |
PARAMÈT SOUDE REKÒMANDE:
DYAMET SPECIFICATIONS (mm) | 2.0 * 250 | 2.6 * 300 | 3.2 * 350 | 4.0 * 350 | 5.0 * 350 | |||||||
ELEKTRISITE (Amp) | H/W | 50-75 | 70-95 | 80-120 | 110-160 | 160-190 | ||||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |
Detay anbalaj:
SEPSIFIKASYON | LONGÈ | PCS/1KG | PWA/1KG | |||
2.0mm | 300mm | 79PCS | 2KG | |||
2.6mm | 300mm | 48PCS | 2KG | |||
3.2mm | 350mm | 27PCS | 5KG | |||
4.0mm | 350mm | 16PCS | 5KG | |||
5.0mm | 350mm | 12PCS | 5KG |
REMAK:
H/W: pozisyon orizontal soude
O/W: soude pozisyon sou tèt