Aliminyòm alyaj TIG ER5356 Welding jointing
KONPONÈ CHIMIK:
ALLOY (poids%) | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Be | S |
RÈG GB/T | 0.25 | 0.40 | 0.10 | 0.05-0.2 | 4.5-5.5 | 0.05-0.2 | 0.10 | 0.06-0.2 | 0.0005 | Marge |
RÈG AWS | 0.25 | 0.40 | 0.10 | 0.05-0.2 | 4.5-5.5 | 0.05-0.2 | 0.10 | 0.06-0.2 | 0.0008 | Marge |
EGZANP VALÈ | 0.15 | 0.10 | 0.03 | 0.15 | 5.2 | 0.1 | 0.05 | 0.12 | 0.0003 | Marge |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | Paran metal | ELONGATION (%) | Tretman chalè | ||||||
RÈG GB/T | - | - | - | - | - | ||||||
RÈG AWS | - | - | - | - | - | ||||||
EGZANP VALÈ | 105 | 205 | 2014-0 | 17 | AW |
Eleman prensipal la se ALMg5Cr.
k5% mayezyòm Distribisyon ak Forge aliminyòm alyaj soude oswa sifas sifas, materyèl inivèsèl soude, gwo fòs, bon malleabilite, bon rezistans korozyon.
Lis fil manje, konbisyon arc ki estab, Splash raman fòme bèl.
-
Materyèl soude pou alyaj aliminyòm
-
Réacteurs polypropylène
-
Gansu Lanke Petrochemical -50 ℃ pwopan pwojè tank esferik
KONPONÈ CHIMIK:
Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Be | S | |
RÈG GB/T | 0.25 | 0.40 | 0.10 | 0.05-0.2 | 4.5-5.5 | 0.05-0.2 | 0.10 | 0.06-0.2 | 0.0005 | Marge |
RÈG AWS | 0.25 | 0.40 | 0.10 | 0.05-0.2 | 4.5-5.5 | 0.05-0.2 | 0.10 | 0.06-0.2 | 0.0008 | Marge |
EGZANP VALÈ | 0.15 | 0.10 | 0.03 | 0.15 | 5.2 | 0.1 | 0.05 | 0.12 | 0.0003 | Marge |
PWOPRIYETE MEKANIK:
PWOPRIYETE | FÒS RENDE (MPa) | FÒS ekstansyon (MPa) | Paran metal | ELONGATION (%) | Tretman chalè | ||||||
RÈG GB/T | - | - | - | - | - | ||||||
RÈG AWS | - | - | - | - | - | ||||||
EGZANP VALÈ | 105 | 205 | 2014-0 | 17 | AW |